The effect of using data palm waste fibers in plain concrete mixture by comparing three pre

Scientific Reports volume 13, Article number: 12032 (2023) Cite this article

The high rates of industrial and agricultural wastes and byproduct production produced several environmental concerns in addition to increasing the risks of contaminating natural resources. The amount of organic waste has been rising over the past few decades, but it has been poorly managed, especially in smaller countries where it is either burned, improperly disposed, or thrown in landfills. Moreover, the production of concrete generates a large amount of waste that has a negative impact on our planet even though it is an extremely significant building material. The potential of developing another plain concrete mixture sample with date palm mesh addition to create more environmentally friendly concrete with better qualities. In addition to using experimental quantitative research to measure the effectiveness of various concrete mixes after adding palm tree residues that underwent biological, chemical, & mechanical treatments, a theoretical qualitative method was also employed in this study to evaluate and identify the ideal mixture design. The prototypes' strength, density, thermal conductivity, slump, and absorption rate were all measured during the experiments. Having a lower heat conductivity and greater strength, the mechanically treated fibers with a 0.6% addition provided the best prototype, according to the research findings.

The increasing human population, consumption rate and human actions in countries all over the world resulted in the production an average of 38 billion metric tons of organic wastes per year1. Several researchers have studied various methods of using agricultural waste to develop environmentally friendly concrete mixtures with adequate strength and better mechanical qualities while having minimal environmental impact. Researchers have experimented methods of partially replacing cement content with palm wastes in order to manufacture environmentally friendly concrete to reduce the waste generated by cement production. The goal of this study is to reduce the environmental impact of palm wastes by using them as a component to the mixture of plain concrete, while also figuring out how to properly dispose and recycle organic wastes and byproducts and enhancing the qualities of plain concrete. In order to create the best sample, which has greater strengths and properties compared to the standard plain concrete but with a reduced thermal conductivity, a detailed assessment of organic wastes, cement, and plain concrete will be presented in this study, along with recommendations for combining them to reduce their environmental impact. The findings and results will help create a prototype sample that will be examined and contrasted with the control concrete mixture2.

Despite the existing 66 composting plants less than 25% of the organic waste in Egypt are being recycled3. The projection study of the solid waste generation in Fig. 1 below shows that by 2025 the organic wastes will exceed 30 million tons per year4. The improper discarding and burning of organic waste resulted in various environmental & health problems5.

Composition (left) and performance (right) of MSW in Egypt as reported in 20105.

There are three types of organic wastes which are the household organic waste, the agriculture organic waste, and the Industrial organic waste, studies show that 50% of organic wastes consists of agricultural wastes6.

The most important agriculture crops that are produced in Egypt are listed in Fig. 2 below along with their annual generation amounts. Egypt produces around 0.66 million tons of date palm residues7.

Types of agricultural waste and percentage of it in Egypt8.

Egypt is the world's biggest producer of date palm fruit. Egypt's yearly date production increased by 70% in 2019, accounting for nearly 30,000 tons9. A single adult date palm tree when trimmed regularly can produce approximately 25 kg of waste per year9. In 2012 Egypt produced 1.47 million tons of dates which makes it the major date producer in the world since it presented one-fifth of the world’s production. The date palm rachis has a long history of being used in the handmade arts, ornaments, baskets, crates, and furniture10. The industrialized wooden strips that are made from the date palm rachis are used to make floorings that is an alternative to the timber floorings, and in the countryside, housings use the palm rachis as a covering material for their roofs.

Figure 3 illustrates the four parts of the date palm where fibers can be extracted: the mesh, the spadix stems, the midribs, and the leaflets. A date palm leaf is a compound leaf that includes three sections: the midrib, the midrib base, and the leaflets11.

Date palm parts (a) spadix stems (b) leaflets (c) midribs (d) mesh.

Comparing with the other date palm fiber species, male date palm surface fiber (MDPSF) has the best tensile strength which range between 170 and 300 MPa12. MDPSF can be obtained from the thin tissue that covers the top of the male plant and works as an insulator to protect the palm from the vagaries of weather14. Date palm fibers are usually treated to reduce the limitations and to improve their performance as shown in Fig. 4.

Utilizing palm residues in different industries7.

Concrete is a composite material composed of Portland cement, water, aggregates, and, in some cases, admixtures. The cement and water combine to form a paste that solidifies and bonds the aggregates13. The amount and properties of the materials used, as well as the method placing, finishing, and curing the concrete, all have a direct impact on its quality. Concrete is a versatile building material that can be used for a wide range of agricultural and residential purposes. It can withstand many acids, silage, milk, manure, fertilizers, water, fire, and abrasion with the right materials and techniques. Due to the usage of concrete as a structural material, strength is considered a very important property to have. Concrete's compressive strengths typically range from 2000 to 5000 pounds per square inch (psi), however for sometimes, concrete can be produced to withstand over 10,000 psi14.

Concrete is well known for its abilities to withstand compression; however, it is very week in tension which makes it very likely to shrink or crack since it becomes more fragile the more its strength increases. Accordingly, to increases its ability to withstand tensions stress steel reinforcement was used However, it is not preferred since it is very expensive, and its tremendous permeability can cause corrosions in it. Recently researchers proposed that polyvinyl alcohol (PVA) and polypropylene fibers can be used instead of steel fibers. However, the production of these fibers requires the use of unsustainable chemical compounds14.

There are variety of factors that can affect and control the properties of concrete such as the mix proportions that has a huge effect on the concrete's strength. Such as: Workability of Concrete,

Segregation of concrete, Bleeding in Concrete, Compressive Strength/Concrete grades, Tensile strength of concrete, and Shrinkage of concrete:

The main component of any concrete mixture is the concrete which is known to have major environmental impacts such as: Energy consumption which is the most serious environmental issue associated with cement and concrete production. Cement production is one of the most energy-intensive industries in the world. The manufacture of cement and the subsequent use of fuel for mining and transportations consumes around 1.758 kWh per ton of cement15. The heavy dependence on coal in industry contributes to extremely high emissions of CO2 and Sulphur, among other pollutants15.

CO2 emissions that are produced during the cement manufacturing process are generated from two different sources. The primary source is fossil fuels, which is around 3/4 tons CO2 per ton of cement and calcined into the cement kiln by lime process. The combustion of rotary kilns is the main cause. Around 5% of overall CO2 emissions are accountable to the cement industry. Apart from CO2, both cement and concrete production emit significant amounts of air pollution, with dust being the most visible pollutant which accounts for 360 pounds per ton of cement produced.16. Another environmental problem associated with cement and concrete production is water pollution. Water used for cleaning equipment is sometimes disposed through placing ponds at the batch plant, where the solids settle out16.

The research methodology is classified into two main categories based on the nature of this study: data gathering and data analysis approaches, as indicated in Fig. 5 below, this study is conducted using two methods: qualitative and quantitative.

Research methodology (developed by author, 2023).

The experiment in this study was divided into 2 phases, phase one is the fibers treatments, and phase two is the concrete mixing. The IUCN Policy Statement on Research Involving Species at Risk of Extinction and the Convention on the Trade in Endangered Species of Wild Fauna and Flora were both complied with, in the collection and use of plant samples for this study. In specifically, a non-lethal harvest of palm mesh fibers was carried out in a farm located in Ismailia, Egypt; this species is classified as having "least concern" status in the IUCN Red List Assessment.

The male date palm mesh was collected during the harvesting season of the date palm trees form a farm in Ismailia, Egypt all the fibers were gathered from Sukkari date palms as shown in Fig. 6 below, then 3 types of treatments was used to treat the fibers:

Mechanical, chemical, & biological fibers treatments (developed by author, 2023).

Mechanical treatment: the date palm mesh was soaked in water for 24 h to ensure saturation, then hand-separated and dried at room temperature for another 24 h before being cut into 60 mm pieces. The chemical treatment: the date palm mesh was soaked for 1 h in 1% NaOh at 100 °C, then it was chopped to 60 mm pieces which is the most common size used in literature. While the Biological treatment: the retting process was used to extract the fibers through which the mesh was soaked in water for 20 days to rot, after that it was cleaned, and the fiber was separated and dried under sunlight. Then the fiber was kept at 100 °C for 24 h for partial removal of moisture.

Ten M30 mixtures of plain concrete were created with the addition of male date palm fibre with a 0%, 0.4% (30 gm), 0.6% (45g m), & 0.8% (60 gm) respectively for each type of treatment to create a total of 150 samples. There sample sizes varied to suit the different type of tests, there were 30 cylindrical samples that measured 10 × 10 × 20 cm and was used for the split cylinder tests, 30 cuboid samples that measured 10 × 10 × 50 cm and were used for the flexural strength tests, while 90 cube samples that measured 10 × 10 × 10 cm and was used for the rest of the tests. The material properties of the components used in the concrete mixtures are listed in Table 1 below.

The concrete mixtures were designed according to the Egyptian standard guidelines by using the materials listed in Fig. 7 below.

Materials used in the concrete mixtures (developed by author, 2022).

The slump test: The concrete slump test indicates the consistency of a concrete mixture. This test is done on the fresh concrete after the mixing and is presented in Fig. 8 below.

(A) Slump test, (B) unit weight, (C) absorption rate, (D) compressive strength test, (E) flexural strength test, and (F) split cylinder test (developed by author, 2023).

The unit weight: The weight of concrete required to fill a container of a defined volume is referred to as the unit weight, the unit weight was measured for a 10 × 10 × 10cm cube.

The absorption rate: was measured at the age of 7 and 28 days, through measuring the sample weight before curing then after 7 days, and after 28 days.

The Compressive strength: Concrete’s ability to withstand loads before failing. It was measured for the samples at the age of 7 and 28 days using compression testing machine.

Flexural strength test: Flexural strength is a form of measuring concrete tensile strength since it measures the ability of a plain concrete beams and slabs to withstand bending failure. It was measured for the samples at the age of 28 days using bend test machine.

Split cylinder test: This test is used to determine the lateral tensile stress of concrete; it was measured for the samples at the age of 28 days using compression testing machine.

The box method was used to calculate the heat transition as shown in Fig. 9. The device contains one hot chamber that had a constant temperature output level which is approximately 732.7 C° (measured by Am probe), the heat transition from the hot chamber to the cold chamber was calculated through measuring the temperature of the cold chamber before adding the heat source then measuring it again after 25 min to measure the amount of heat transferred through the samples.

The box method & the Thermometers used to measure the temperature in the box method (developed by author, 2023).

The findings will be presented into two different levels; the experiment conducted, and the observational results noted during the experiment. Slump, absorption, unit weight, compressive strength, flexural strength, tensile strength, and thermal conductivity are the experimental tests of the concrete’s samples with different treatments and percentages of fibres, while comparing them to the control samples. The maximum, average, and minimum experimental results of the tests are illustrated in Table 2 below.

Table 3 below illustrates the comparative analysis between the different percentages and treatments of fibres additions to the concrete mixtures, noting that the durability, cost, environmental impact, and human health impact were evaluated by the authors.

According to this experimental study, The M6 samples has successfully reduced the human health impact and environmental impact while providing lower thermal conductivity and better strength.

This study investigated the possibility of using different treatment methods to treat male date palm fibers in order to utilize them in the plain concrete mixtures in order to improve it physical and mechanical properties and produce ecofriendly concrete through minimizing the harmful effects of improper disposal of organic waste such as the date palm residues, while decreasing the use of cement content since adding the fibers helps in combining the plain concrete’s components and slightly increase the volume of the total mixture. The research experiment added three different percentages of date palm fibers to identify the best combination of treatment and percentages to achieve the ideal prototype with the best physio-mechanical properties. Unlike Alatshan et al.15 work that stated that with increasing fiber percentage and length, the compressive strength decreased while the flexural strength increased. The research finding proved that the best properties were of the samples that included 0.6% mechanical treated fibers, while highlighting that the chemical treatment produced the worst physio-mechanical properties of the concrete samples.

Finally, to complete their investigation, the authors just collected the bare minimum of specimens. All data are available from the corresponding author on reasonable request.

Moussa, R. R. Measuring the economic benefits for reusing organic wastes in generating gas and electricity to create self-sustain city. Int. J. Sustain. Dev. Plan. 17(3), 885–893. https://doi.org/10.18280/ijsdp.170318 (2022).

Article Google Scholar

Elseify, L. A. et al. ‘Review on cellulosic fibers extracted from date palms (Phoenix Dactylifera L.) and their applications. Cellulose 100, 2209–2232. https://doi.org/10.1007/s10570-019-02259-6 (2019).

Article CAS Google Scholar

Elfeki, M. & Tkadlec, E. Treatment of municipal organic solid waste in Egypt. J. Mater. Environ. Sci. 6(3), 756–764 (2015).

CAS Google Scholar

Murali, V. Date Palm Waste as a RE Source in Egypt. A Technical and Economic Analysis (GRIN Verlag, 2021).

Google Scholar

Moussa, R. R. The potential of using anaerobic digesters in developing countries. Clean. Eng. Technol. https://doi.org/10.1016/j.clet.2022.100517 (2022).

Article Google Scholar

Kiyasudeen, K. et al. Applied environmental science and engineering for a sustainable future prospects of organic waste management and the significance of earthworms. In Prospects of Organic Waste Management and the Significance of Earthworms 202–234. http://www.springer.com/series/13085 (2016).

Micheal, A. & Moussa, R. R. Evaluating the effect of adding sugarcane bagasse to the fire clay brick’s properties. Civ. Eng. Archit. HRPUB 10(1), 71–78. https://doi.org/10.13189/cea.2022.100106 (2022).

Article Google Scholar

Abou Hussein, S. D. & Sawan, O. M. The utilization of agricultural waste as one of the environmental issues in Egypt (a case study). J. Appl. Sci. Res. 6(8), 1116–1124 (2010).

CAS Google Scholar

Murali, V. Date Palm Waste as a RE Source in Egypt (GRIN Verlag, 2021).

Google Scholar

Piesik, S. Arish: Palm-Leaf Architecture (Thames & Hudson, 2012).

Google Scholar

El-Mously, H. The industrial use of the date palm residues: an eloquent example of sustainable development. In International Conference on Date Palms 866–886 (2001).

Al-Khayri, J. M., Jain, S. M. & Johnson, D. V. Date Palm Genetic Resources and Utilization Vol. 1 (Springer, 2015).

Book Google Scholar

Dawoud, N., Micheal, A. & Moussa, R.R. A review on investigating the experimental process for partial replacement of cement with sugarcane bagasse in the construction industry. In The International Conference on Civil and Architecture Engineering (ICCAE), Cairo_ Egypt. IOP Conference Series: Materials Science and Engineering Vol. 974. https://doi.org/10.1088/1757-899X/974/1/012036 (2020).

Shelton, D. P. & Harper, J. M. (1982) An overview of concrete as a building material an overview of concrete as a building material

Alatshan, F. et al. Effect of date palm fibers on the mechanical properties of concrete. Int. J. Sustain. Build. Technol. Urban Dev. 8(2), 100. https://doi.org/10.12972/susb.20170007 (2017).

Article Google Scholar

Micheal, A. & Moussa, R. R. Investigating the economic and environmental effect of integrating sugarcane bagasse (SCB) fibers in cement bricks. Ain Shams Eng. J. 12(3), 3297–3303. https://doi.org/10.1016/j.asej.2020.12.012 (2021).

Article Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Environmental Sustainable Architecture Department, Faculty of Energy, The British University in Egypt (BUE), Cairo, Egypt

Dina R. M. Moawad

Architecture Department, Faculty of Engineering, The British University in Egypt (BUE), Cairo, Egypt

Rania Rushdy Moussa

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

D.M. and R.M. wrote the main manuscript text and D.M. prepared all the figures. All authors reviewed the manuscript.

Correspondence to Dina R. M. Moawad.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Moawad, D.R.M., Moussa, R.R. The effect of using data palm waste fibers in plain concrete mixture by comparing three pre-treatment techniques. Sci Rep 13, 12032 (2023). https://doi.org/10.1038/s41598-023-37860-0

Download citation

Received: 07 April 2023

Accepted: 28 June 2023

Published: 25 July 2023

DOI: https://doi.org/10.1038/s41598-023-37860-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.